Chromium Fog Inhibitor GL-F53
- Product No.：GL-F53
GL-F53 chromium fog inhibitor is a kind of environmental protection chromium fog inhibitor made of high-tech new materials. It has the characteristics of high temperature resistance, strong oxidant resistance and electrolytic stability. It is mainly used in the electroplating of hexavalent chromium and the roughening process of plastic electroplating to inhibit the generation of chromium fog
Chromium Fog Inhibitor used for Chrome Plating baths, has the characteristics of high temperature resistance, strong oxidant resistance and electrolytic stability.
Add 0.04g GL-F53 to 1L plating bath, increase the use amount more for the first time, until the solvent up to saturation.For future, it can be added in batches according to the foam consumption.
1. When the product is dissolved and poured into the plating tank, the foam formed within 3-5 minutes can completely cover the surface of the plating solution to preventing the escape of chrome fog. The foam disappears after the electroplating is stopped and the foam will be reappeared when used next time.
2. This product is suitable for chromic acid with a concentration of 250-300 g/L. Exceeding this concentration range will affect the service life.
3. The temperature of the electroplating solution is 40℃ -60℃.
4. Adding GL-F53 should not be too much, that is, the thickness of the foam should not exceed three centimeters. The electrode of the plated part must be in good contact to prevent sparks and maintain air circulation to prevent the accumulation of hydrogen and cause knocking.
Dissolve the weighed GL-F53 powder completely with boiling water (for example, add 20 grams of GL-F53 powder to about 500 milliliters of boiling water), then put it into the plating bath.
10kg/box or 10kg/drum(Normal), stored away from light.